Direct Forming Tube Mill (150x150mm)

(1)Raw material

Material Quality

Q195、Q235B、Q355B、Galvanized Steel、MS、CR、HR

Mechanical properties

σb≤500Mpa，σs≤325MPa

Strip Width

280-600mm

Strip Thickness

2.0-6.0mm

Coil ID

Φ508-610mm 

Coil OD

Φ1200mm-2100mm

Coil Weight

10.0T

(2)Finished Product Size and purpose

Tube Size

70x70-150x150mm     T:2.0-6.0 mm

Length

4-6m

Application

Structure

(3)The working process of the production line

Raw material (strip)→Coil loading(coil Ramp& coil car)→ Uncoiler→Coil peeler and head straightener→Pinch and leveler→Shear and welder→ Accumulator → passive leveling → Forming →High frequency welding → External scarfing & ironing →Water cooling →Sizing→Turks head→ Milling saw→Conveyor(run out table) →Punching hole →Full auto packing(stacking and strapping)

(4)Forming type

(5)This line contain

Coil conveyor car

The coil conveyor car is used for make the steel coil from loading position to uncoiler.at the same time loft oil cylinder,so that the steel coil inner hole is accurately set on the cone of uncoiler, after the uncoiler tension, push back to the original position.

Uncoiler

Expansion and cantilever mandrels.

Contains two main parts: main body and the fixed base.

Equipped with pneumatic system to satisfy the needs of expanding, contracting and braking of the mandrels.

Mandrel consists of four-bar linkages that could move radially at the same time.

The four-bar linkages in two groups are fitted on two shafts respectively. Powered by air cylinder, they expand and contract radially.

Straight head machine

This machine is used to open the coil head and smoothly introduce the next device to a smooth machine. The pressure roller on the head is mainly used to press the head of the roll to prevent the scatter roll from scattering, and the shovel is shovel smoothly. The pressure roller rotates under the motor. For the opening machine, it is a help roller. There is a straight head roller, which is mainly the curved pressure of the head of the steel, cooperate with the shovel header, and make it forward along the shovel. The guide roller leads the material into the next process.

Pinch leveling machine

The pinching machine is divided into three parts: clamping materials, the flat house roller, and the flattering machine transmission. The five -roller smoothing can change the passing steel through the up and down adjustment of the five rollers to a straight state, and the transmission part of the ingening machine provides motivation for the pinhris roller and the flat roller.

Automatic shear and welder

It is used to cut the irregular ends of the strips and then connect the strips by welding. So it can let the line runing without stop when the before coil finish.

Spiral accumulator

This machine is between shear welder and host (forming sizing mill) ，use for after a roll of strip steel are used up, before the next roll strip since prepared from uncoiling, shearing and butt welding time to ensure that the host (forming sizing mill) continuous production and store enough strip steel.

Forming and sizing mill

Forming & Sizing Mill adopts roller type forming principle and high-frequency induction welding. The strip is fed into the forming machine by the feeding device in the mill and the forming roller continuously rotate and press the strip into the required shape. Due to the skin and the kindred effect, the high-frequency current is concentrated on the weld joint that is heated rapidly and reaches the welding temperature. The tube seam is welded under the pressure of squeeze rollers. The finished welded tube with required size can obtained after the cooling, sizing and primary straightening.

Cutting saw

It is used to precisely cut the pipe to length automatically under the condition that the pipe continuously delivered from the mill at high speed.

600 kw Hifrequency Welder

Weld the seam

Runout Transit table

Transit the finished pipe to the collection table